SikaTop®-111 Plus Mortar

Description

PICK UP ONLY IN MOUNT VERNON NEW YORK 10550
SikaTop®-111 Plus is a two-component, polymer-modified, Portland cement-based, fast-setting, screed mortar. It is a high performance repair mortar for horizontal, vertical and overhead surfaces in form and pour applications. It offers the additional benefit of Sika FerroGard®-901, a penetrating corrosion inhibitor included in its formulation.
Usage
On grade, above grade, and below grade concrete
Horizontal surfaces (e.g. for spall repairs on flat work, or as an overlay): pour and screed
Vertical and overhead surface repairs when formed and poured, or formed and pumped with an appropriate pump
Structural repair material for water and wastewater treatment plants, parking facilities, industrial plants, walkways, bridges, tunnels, dams, abutments, floors and balconies
Approved for repairs over cathodic protection systems
Free flowing repair mortar for hard-to-reach areas
Filler for voids and cavities
Repair of substrates such as concrete, mortar, and masonry
Advantages
Extremely low shrinkage proven by four industry standard test methods
High compressive and flexural strengths
Increased freeze/thaw durability and resistance to deicing salts
Increased density - improved carbon dioxide resistance (carbonation) without adversely affecting water vapor transmission (not a vapor barrier)
Enhanced with Sika FerroGard®-901, a penetrating corrosion inhibitor - reduces corrosion even in the adjacent concrete
Packaging
SikaTop® 'A' Component:  1 gallon (3.8 liters) plastic jug; 4 jugs/carton
SikaTop®-111 Plus 'B' Component:  61.5 lb (27.9 kg) bag
Color
'A' Component:  White liquid    'B' Component:  Gray powder
'A' + 'B' mixed:  Gray mortar
Product Details
Sustainability / Certifications / Approvals
APPROVALS / STANDARDS
Compatible with coefficient of thermal expansion of concrete - Passes ASTM C 884
USDA certifiable for incidental food contact
Independently certified for NSF/ANSI 61 (potable water) compliance
Product Information
Technical Information
Application
Application Information
Mixing Ratio
7/8 - 1 gallon (3.3 - 3.8 liters) of 'A' Component : 61.5 lbs (27.9 kg) of 'B' Component
Fresh Mortar Density
136 lb/ft
3
(2.18 kg/l)
(ASTM C 138)
73
o
F (23
o
C),
50% R.H.
Layer Thickness
Minimum
Maximum in one lift *
Neat
1/2 inch (12 mm)
1 inch (25 mm)
Extended
1 inch (25 mm)
6 inches (152 mm)
* If repair requires multiple lifts, each lift should be applied as soon as the previous lift has developed enough initial strength to support it.
Product Temperature
65° - 75° F (18° - 24° C)
Ambient Air Temperature
40° - 95° F (4° - 35° C)
Substrate Temperature
40° - 95° F (4° - 35° C)
Set Time
40 – 70 minutes
(ASTM C 266)
73
o
F (23
o
C),
50% R.H.
Final Set Time
> 90 minutes
(ASTM C 266)
73
o
F (23
o
C),
50% R.H.
Application Time
Approximately 30 minutes
Temperature will affect the Application Time:
Above 73° F (23° C) will reduce the Application Time and slump
Below 73° F (23° C) will extend the Application Time and slump
Finishing Time
50 – 120 minutes
Waiting / Recoat Times
Refer to Sika Tech Brief # 18-01 for minimum cure times prior to overcoating.